大清雍正茶叶末釉赏瓶     高:39.5cm   口径:16cm 

茶叶末釉是我国古代铁结晶釉中重要的品种之一,属高温黄釉,经高温还原焰烧成。以氧化铁为呈色剂,经1200℃—13

00℃之间高温还原焰烧制而成。釉面呈失透状,釉色黄绿掺杂似茶叶细末,绿者称茶,黄者称末,古朴清丽,耐人寻味。深沉凝重,极具古意。雍正,乾隆两朝最为所重,成为宫廷秘釉,仅供皇室珍赏。茶叶末釉其标准样品在大多数情况下是一种棕黑色底或绿黑色底釉中泛现一种错落自然,金光灿烂的黄绿色晶点。茶叶末的烧成难度较大,低温阶段用氧化气氛烧制,到980℃左右以后,若转为还原气氛烧制,则发墨绿色晶点俗称"蠏甲青"。若继续氧化烧成则发黄色晶点俗称"鳝鱼黄"。瓶敞口,长颈,溜肩,圆腹,造型端庄。通体施茶叶末釉,釉色莹润。在清代赏瓶中多见青花和粉彩,而茶叶末釉赏瓶却十分少见。

The final glaze appreciation bottle height of yongzheng tea in qing dynasty is 39.5cm in diameter: 16cm

Tea final glaze is one of the important types of ancient iron crystal glaze in China. Based on iron oxide coloring agent, after 1200 ℃ - 13

00 between ℃ high temperature reducing flame burn becomes. The glaze is opaque, the glaze color yellow green doping like the fine tea powder, the green tea, the yellow tea, the last, the primitive simplicity qingli, interesting taste. Deep and solemn, very ancient. Yongzheng and qianlong dynasties were the most important, becoming the secret glaze of the court, which was only appreciated by the royal family. In most cases, the standard sample of tea final glaze is a kind of brown black bottom or green black bottom glaze in which there is a kind of natural dislocation and bright yellow and green spots with golden light. Tea at the end of the firing is difficult, the low temperature stage in oxidizing atmosphere fire, to about 980 ℃, if, to reducing atmosphere burn is crystal FaMo green point commonly known as "蠏 armored". If continue to oxidize burn into, then hair yellow crystal point commonly known as "eel yellow". Bottle open, long neck, slip shoulder, round abdomen, dignified shape. Apply the final glaze of tea, the glaze is bright and smooth. In the qing dynasty, there were many blue and white flowers and powder colors in the appreciation bottle, but the glaze appreciation bottle at the end of tea was very rare.